英文:Superparamagnetic magnesium ferrite/silica core-shell nanospheres: A controllable SiO2 coating process for potential magnetic hyperthermia application 
著者
和文: Harinarayan Das, Nipa Debnath, Takashi Arai, 川口 昂彦, 坂元 尚紀, 篠崎 和夫, 鈴木 久男, 脇谷 尚樹.  
英文: Harinarayan Das, Nipa Debnath, Takashi Arai, Takahiko Kawaguchi, Naonori Sakamoto, Kazuo Shinozaki, Hisao Suzuki, Naoki Wakiya.  
言語 English 
掲載誌/書名
和文: 
英文: 
巻, 号, ページ Vol. 30    No. 12    pp. 3171-3181
出版年月 2019年10月5日 
出版者
和文: 
英文:Elsevier 
会議名称
和文: 
英文: 
開催地
和文: 
英文: 
DOI https://doi.org/10.1016/j.apt.2019.09.026
アブストラクト The control of coating shell becoming important to improve the applicability of magnetic nanoparticles. Herein, we present the scalable technique for preparing MgFe2O4/SiO2 core-shell nanospheres with finely tuned shell thickness and their efficiency in magnetic hyperthermia heating agent. At first, MgFe2O4 dense nanosphere derived from one-step ultrasonic spray pyrolysis (USP) technique. Silica shells were then coated on the as prepared nanospheres with tunable thickness from 10 to 30 nm. We show that the thickness of this coating is finely controlled at allowing our proposed level by using the required amount of SiO2 precursor (SiC8H20O4)/acidic catalyst (HCl) ratio where the surface area of core nano- spheres are significantly considered. X-ray diffraction reveals the cubic spinel ferrite structure of core particles with crystallite size 9.6 ± 1.8 nm and Fourier transform infrared spectrum analysis confirmed the formation of SiO2. The morphological observation clarified the uniform and smooth SiO2 shell where core-shell nanostructure is highly monodispersed in a liquid medium. M-H loops confirmed the super- paramagnetic nature of all samples at room temperature. Significantly reduced ion release concentration in an aqueous solvent of the coated nanospheres compared with uncoated sample demonstrates the her- metically coating feature of dense SiO2. This MgFe2O4/SiO2 core-shell nanospheres with thine SiO2 shell (10 nm) shows effective heating rate in the operative region (<46 C) which makes them promising can- didates for application as magnetic hyperthermia heating agent.